Triple perovskite CoSr2YCu2O<f>7−δ</f> and its peculiar structural features: a neutron diffraction study.

Samples of the composition CoSr2YCu2O<f>7−δ</f> (Co-1212) were synthesized in a single-phase form and studied using neutron diffraction (ND), chemical analyses and magnetization measurements. The structure of Co-1212 is best described in the space group Ima2 that yields good fit to the observed ND data. No cross-migration between Cu and Co is seen for Co-1212. The overall oxygen content, as determined from the refined oxygen occupancies, comes out to be around 7.0. This is close to the values determined from wet-chemical and thermogravimetric analyses. Unlike in Cu-1212, the complete reduction of Co-1212 in 5% H2/95% Ar atmosphere occurs in a single step, revealing that the amount of reversibly removable oxygen is considerably less than that in Cu-1212. Zero-field-cooled and field-cooled magnetizations, measured in an applied field of 100 Oe, show branching at around 30 K, presumably due to the magnetic ordering of Co moments. The present Co-1212 sample is found not to be superconducting down to 5 K. [ABSTRACT FROM AUTHOR]