Effect of blowing agents on the oxidation resistance of carbon foams prepared from molten sucrose.

We have prepared low density carbon foams from molten sucrose using aluminium nitrate and boric acid blowing agents. A comparative study of the oxidation resistance of the carbon foams prepared using the two blowing agents are reported in the present paper. Oxidation of the carbon foams was evaluated under isothermal and non-isothermal conditions in air atmosphere using thermogravimetric analysis (TGA). We have observed that the alumina produced from the aluminium nitrate blowing agent acts as a catalyst whereas the boron produced from boric acid inhibits the oxidation of the carbon foams. The oxidation resistance of carbon foams increases with boron concentration. The oxidation onset temperature for the carbon foams prepared using boric acid blowing agent was nearly 60°C higher than that prepared using aluminium nitrate blowing agent. Carbon foams prepared using aluminium nitrate blowing agent undergoes complete oxidation at temperature less than 700°C. Whereas that prepared using boric acid blowing agent leave ∼ 50 wt.% residue at 900°C. Further evidence is provided by the kinetic analysis of the TGA using Coats-Redfern (CR) equation. [ABSTRACT FROM AUTHOR]