Fabricating fine-grained tungsten heavy alloy by spark plasma sintering of low-energy ball-milled W–2Mo–7Ni–3Fe powders.

Abstract: Fine-grained W–2Mo–7Ni–3Fe heavy alloys were fabricated by low-energy ball milling (LEBM)-assisted spark plasma sintering at a temperature range of 1000–1250°C. The effects of sintering temperature on the phase evolution, microstructural characteristics, and mechanical properties of the alloys were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), hardness testing, and universal testing. The XRD results show that small intermetallic compounds, such as NiW and Ni2W4C, form in the alloys. The W–2Mo–7Ni–3Fe alloys are characterized by white W grains, a gray W-rich microstructure that contains Mo, and a black γ–(Ni, Fe, W, Mo) binding phase. The X-ray energy dispersive analysis (EDS) shows that the Mo, Ni, and Fe that form a solid solution with W in the gray structure gradually decrease with increasing temperature. The hardness and bending strength of the alloys initially increase and then decrease with rising sintering temperature. Moreover, the alloys sintered at different temperatures exhibit dissimilar bending fracture modes. [Copyright &y& Elsevier]