Microstructure and mechanical behavior of commercial purity Ti/Ti–6Al–2Zr–1Mo–1V structurally graded material fabricated by laser additive manufacturing.

The mechanical behavior of commercial purity Ti (CP-Ti)/Ti–6Al–2Zr–1Mo–1V structurally graded materials (SGMs) fabricated by laser additive manufacturing was investigated via uniaxial tensile experiments. Although the strength of all SGM specimens is higher than that of the monolithic CP-Ti specimens, only the SGM specimen of Ø10mm gauge diameter with bulky α-grains exhibits excellent plasticity comparable to the CP-Ti specimen under the same conditions. The SGM presents a potential for use as load-bearing components due to its good strength–ductility balance. [ABSTRACT FROM AUTHOR]