Interfacial orientation and misorientation relationships in nanolamellar Cu/Nb composites using transmission-electron-microscope-based orientation and phase mapping.
- Source :
-
Acta Materialia . Feb2014, Vol. 64, p333-344. 12p. - Publication Year :
- 2014
-
Abstract
- Abstract: A transmission-electron-microscope-based orientation mapping technique that makes use of beam precession to achieve near-kinematical conditions was used to map the phase and crystal orientations in nanolamellar Cu/Nb composites with average layer thicknesses of 86, 30 and 18nm. Maps of high quality and reliability were obtained by comparing the recorded diffraction patterns with pre-calculated templates. Particular care was taken in optimizing the dewarping parameters and in calibrating the frames of reference. Layers with thicknesses as low as 4nm were successfully mapped. Heterophase interface plane and character distributions (HIPD and HICD, respectively) of Cu and Nb phases from the samples were determined from the orientation maps. In addition, local orientation relation stereograms of the Cu/Nb interfaces were calculated, and these revealed the detailed layer-to-layer texture information. The results are in agreement with previously reported neutron-diffraction-based and precession-electron-diffraction-based measurements on an accumulated roll bonding (ARB)-fabricated Cu/Nb sample with an average layer thickness of 30nm as well as scanning-electron-microscope-based electron backscattered diffraction HIPD/HICD plots of ARB-fabricated Cu/Nb samples with layer thicknesses between 200 and 600nm. [Copyright &y& Elsevier]
Details
- Language :
- English
- ISSN :
- 13596454
- Volume :
- 64
- Database :
- Academic Search Index
- Journal :
- Acta Materialia
- Publication Type :
- Academic Journal
- Accession number :
- 93419707
- Full Text :
- https://doi.org/10.1016/j.actamat.2013.10.046