Preparation of biomorphic silicon carbide–mullite ceramics using molten salt synthesis.

Abstract: Biomorphic silicon carbide–mullite ceramics were prepared from beech wood using liquid Si infiltration and molten salts synthesis. The resulting mullite whiskers coating, as well as the growth mechanism in molten Al2(SO4)3–Na2SO4 environment, have been investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) techniques. The biomorphic SiC ceramics derived from the beech wood template have coarse pore walls consisting of β-SiC grains with diameters ranging from 5 μm to 20 μm. After the molten salts reactions between biomorphic SiC substrate and mixture molten salts (Al2(SO4)3–Na2SO4), porous Silicon carbide–mullite ceramics with cilia-like microstructure were obtained. This unique structure has potential application in hot gases filters. An oxidation–dissolution cycle was proposed to explain the mullite whiskers growth in molten salts environment. [Copyright &y& Elsevier]