Structural, optical, and magnetic properties of highly-resistive Sm-implanted GaN thin films.
- Source :
-
Journal of Applied Physics . 2014, Vol. 116 Issue 4, p043909-1-043909-8. 8p. 7 Graphs. - Publication Year :
- 2014
-
Abstract
- Samarium ions of 200 keV in energy were implanted into highly-resistive molecular-beam-epitaxy grown GaN thin films with a focused-ion-beam implanter at room temperature. The implantation doses range from 1×1014 to 1×1016cm-2. Structural properties studied by x-ray diffraction and Raman-scattering spectroscopy revealed Sm incorporation into GaN matrix without secondary phase. The optical measurements showed that the band gap and optical constants changed very slightly by the implantation. Photoluminescence measurements showed emission spectra similar to p-type GaN for all samples. Magnetic investigations with a superconducting quantum interference device identified magnetic ordering for Sm dose of and above 1×1015cm-2 before thermal annealing, while ferromagnetism was only observed after thermal annealing from the sample with highest Sm dose. The long-range magnetic ordering can be attributed to interaction of Sm ions through the implantation-induced Ga vacancy. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00218979
- Volume :
- 116
- Issue :
- 4
- Database :
- Academic Search Index
- Journal :
- Journal of Applied Physics
- Publication Type :
- Academic Journal
- Accession number :
- 97312173
- Full Text :
- https://doi.org/10.1063/1.4891226