Ru supported on zirconia-modified SBA-15 for selective conversion of cellobiose to hexitols.

Ru supported on zirconia-modified SBA-15 as a catalyst for selective conversion of cellobiose has been prepared and characterized using X-ray diffraction, N 2 adsorption, transmission electron microscopy, and temperature programmed desorption of NH 3 . Coating SBA-15 with zirconia generates acid sites as well as improves Ru dispersion in the mesopore. At a Zr/Si ratio of 0.25 (∼1.4 monolayer coverage of zirconia on the SBA-15 surface), the mesoporous structure of SBA-15 was well preserved in zirconia-modified SBA-15. Increasing the amount of zirconia beyond Zr/Si = 0.5 resulted in narrowing of the mesopores and, eventually, pore blockage. Mechanistic study of cellobiose conversion on the catalyst indicates that the reaction proceeds sequentially through (a) hydrogenolysis/hydrogenation of cellobiose to 3-β- d -glucopyranosyl- d -glucitol, (b) hydrolysis to sorbitol and glucose, and (c) glucose hydrogenation to hexitols, with the hydrolysis step being the rate-determining step for hexitols formation. A complete conversion of cellobiose with a hexitols yield of 72% has been achieved at 140 °C in 1 h with the optimal Zr/Si ratio of 0.25. A comparison with the more acidic Ru/HZSM-5 catalyst demonstrated the importance of the mesopores of SBA-15 to the catalytic reactivity of Ru/Zr-SBA-15(0.25). [ABSTRACT FROM AUTHOR]