The effect of suspended Fe3O4 nanoparticle size on magneto-optical properties of ferrofluids.

We investigate the effect of hydrodynamic particle size on the magnetic field induced light transmission and transmitted speckle pattern in water based ferrofluids containing functionalized Fe 3 O 4 nanoparticles of size ranging from 15 to 46 nm. Three water-based magnetic nanofluids, containing Fe 3 O 4 nanoparticles functionalized with poly-acrylic acid (PAA), tetra-methyl ammonium hydroxide (TMAOH) and phosphate, are used in the present study. In all three cases, the transmitted light intensity starts decreasing above a certain magnetic field (called first critical field) and becomes a minimum at another field (second critical field). These two critical fields signify the onset of linear aggregation process and zippering transitions between fully grown chains, respectively. Both these critical fields shift towards a lower magnetic field with increasing hydrodynamic diameter, due to stronger magnetic dipolar interactions. The first and the second critical fields showed a power law dependence on the hydrodynamic diameters. The dipolar resonances occurring at certain values of the scatterer size, leads to the field induced extinction of light. Both the onset of chaining and zippering transitions were clearly evident in the time dependent transmitted light intensity. Above the first critical field, the lobe part of the transmitted intensity and the lobe speckle contrast values increase with increasing external magnetic field due to reduced Brownian motion of the field induced aggregates. The speckle contrast was highest for nanoparticle with the largest hydrodynamic diameter, due to reduced Brownian motion. These results provide better insight into field dependent light control in magnetic colloids, which may find interesting applications in magneto-optical devices. [ABSTRACT FROM AUTHOR]