Long-term resistance to fracture and/or corrosion of the nitinol wires of the talent stent-graft: observations from a series of explanted devices.

The biodurability of the Nitinol wires used in stent-grafts retrieved from reoperations and autopsy was analyzed to assess the possible causes of fracture and/or corrosion of the stents. The Nitinol wires of six explanted devices presented a corrosion-free surface after in vivo service. The drawing lines in the control wires were still present, but neither burrs nor flakes were observed. Pits and crevices were rare, but some shallow ones were present. Some abrasions of the surfaces of the Nitinol wires were also observed. The chemical composition of the explanted devices showed the presence of organic contamination that covered the thick layer of titanium oxide before reaching the Nitinol itself. The durability of the Nitinol employed in the manufacture of the Talent stent-grafts was confirmed; the results of this study show the Nitinol to be resistant to corrosion. We have also concluded that the fractures of the Nitinol wires in two devices were unique adverse incidents caused by compression and bending related to the sharp angle of the Nitinol wires.