Calculation of Volume Fractions of In Situ TiB and Residual Stress Distributions in Functionally Graded Composite of Ti-TiB-TiB 2 .

Ti matrix composite with a polylaminate structure was successfully fabricated via spark plasma sintering (SPS) process. A temperature gradient field (TGF) was obtained during the sintering to form functionally graded material (FGM) in a vacuum under 40 MPa for 5 min. The actual volume fractions of TiB in the matrix were calculated based on the X-ray diffraction pattern. The target volume fractions of TiB were 0%, 20%, 40%, 60%, 80% and 100%. The calculated TiB volume fractions were slightly higher than the target volume fractions in layers 2-4 and lower than the target volume fractions in layers 5-6 and the deviations in layers 4 and 5 were less than 5% of the target volume. Based on the elastic axial symmetry model, the residual stress distributions in the Ti matrix composite with a polylaminate structure were simulated, indicating a relatively low thermal residual stress in the FGM.