Photocatalytic aging process of Nano-TiO 2 coated polypropylene microplastics: Combining atomic force microscopy and infrared spectroscopy (AFM-IR) for nanoscale chemical characterization.
- Source :
-
Journal of hazardous materials [J Hazard Mater] 2021 Feb 15; Vol. 404 (Pt B), pp. 124159. Date of Electronic Publication: 2020 Oct 02. - Publication Year :
- 2021
-
Abstract
- Microplastics (MPs) are considered to have greater environmental hazards than large plastics. Most MPs undergo different degrees of aging and aged MPs exhibit different physicochemical properties from pristine ones. This study successfully prepared a nano-TiO <subscript>2</subscript> coated polypropylene MPs, and explored the nanoscale infrared, thermal, and mechanical properties of MPs before and after photo-aging using a combined AFM-IR technique. Surface height range of MPs was ± 25 nm. The signal intensity of the absorption peak at 1654 cm <superscript>-1</superscript> in terms of vinylidene end groups gradually increased as the irradiation time prolonged. The softening temperature of MPs decreased from 126.7 °C to 108.5 °C as the irradiation time increased from 0 h to 4 h. The MPs after photo-aging became stiffer, especially for the components surrounding the nano-TiO <subscript>2</subscript> particle, indicating that photocatalytic reaction accelerated the aging process of MPs. The resonance frequency of MPs surrounding the nano-TiO <subscript>2</subscript> particle was stronger after photo-aging and the stiffer components were uniformly distributed, confirming that the thermal and mechanical properties of MPs changed after photo-aging. These novel findings are essential to better understand the changes in the surface microstructures, physical properties, and chemical compositions of MPs during aging process.<br /> (Copyright © 2020. Published by Elsevier B.V.)
Details
- Language :
- English
- ISSN :
- 1873-3336
- Volume :
- 404
- Issue :
- Pt B
- Database :
- MEDLINE
- Journal :
- Journal of hazardous materials
- Publication Type :
- Academic Journal
- Accession number :
- 33080556
- Full Text :
- https://doi.org/10.1016/j.jhazmat.2020.124159