Effect of core and surface area toward hydrogen gas sensing performance using Pd@ZnO core-shell nanoparticles.

A versatile hydrogen gas sensor is fabricated using Pd@ZnO core-shell nanoparticles (CSNPs), which were synthesized through a hydrothermal route. Effect of oxidation behavior of Pd core to hydrogen sensing is also investigated for Pd@ZnO CSNPs. Accordingly, Pd@ZnO-2 sensor (core-shell sample was calcined in argon) demonstrates the best performance with respect to Pd@ZnO-1 (core-shell sample was calcined in air) and pure ZnO. It shows a much higher response (R = R _a /R _g  = 22) than those of Pd@ZnO-1 (12) and pure ZnO (7) sensors with faster response and recovery times (1.4 and 7.8 min) to 100 ppm hydrogen at 350 °C. In addition, Pd@ZnO-2 sensor owns high selectivity to hydrogen among interfering target gases. Improvement can be attributed to the high content of metallic Pd ⁰ species in CSNPs as calcined in argon. Thereby, a higher Pd metallic content (77%) still remains in Pd@ZnO-2 compared to Pd@ZnO-1 (56%), which in turn modulates the resistance of sensors as exposed to air and target gas, thus enhancing gas sensing activity. High BET surface area of core-shell materials provides plenty of active sites for accelerating the sensing reactions as well.
Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
(Copyright © 2020 Elsevier Inc. All rights reserved.)