Effect of erosive media on microhardness and fracture toughness of CAD-CAM dental materials.

Background: Erosive acids might create surface flaws and deteriorate the mechanical properties of CAD-CAM materials. This invitro study aimed to investigate the effect of simulated gastric HCl and extrinsic erosive acids on surface microhardness and fracture toughness of CAD-CAM materials.
Methods: 400 bar-shaped specimens (17×4×2 mm ³ ) were prepared from 4 different CAD-CAM dental materials (n = 100/group); monolithic zirconia (Ceramill Zolid HT+, Amanngirbach, Austria), lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein), nanohybrid resin composite (Grandio Blocs, VOCO) and polymer-infiltrated glass network (Vita Enamic, VITA Zahnfabrik). Specimens from each material type were further subdivided into 5 groups (n = 20) according to the erosive media applied (simulated gastric HCl, white wine, Coca-Cola®, orange juice, and artificial saliva that served as a control). Specimens were immersed for 24 h in an incubator at 37 ℃, then ultrasonically cleaned in distilled water and air-dried. Half of the specimens were tested for Vickers microhardness (VHN) at parameters of 500 gf for 10 s, while the rest of the specimens underwent 3-point flexure till fracture. Fractured surfaces were examined under a scanning electron microscope (SEM) for fracture toughness (K _IC ) calculation using the quantitative fractographic analysis method. Data collected were statistically analyzed using two-way analysis of variance (α = 0.05) after verification of data normality and homogeneity of variances.
Results: Erosive media created surface flaws that lowered the surface microhardness of the material and initiated the fracture pattern under different loads according to material type. The material type was a more predominant factor than erosive media that affected either the microhardness or the fracture toughness of CAD-CAM dental materials. The highest VHN and K _IC values were found among Ceramill Zolid HT+ groups followed by IPS e.max CAD and Grandio Blocs regardless of the erosive media employed. Erosive media significantly reduced the VHN and K _IC in Vita Enamic specimens compared to the rest of the material types.
Conclusion: All CAD-CAM materials used, except Vita Enamic, showed high resistance against the erosive acids indicating higher longevity of the material in patients frequently exposed to either extrinsic or intrinsic acid.
(© 2022. The Author(s).)