Strong oxygen-content dependence of the magnetic excitations in antiferromagnetic NiO nanoparticles: A Raman probe.

Nanostructured antiferromagnetic (AFM) NiO has attracted much attention from both the fundamental and applied perspectives. Understanding the two-magnon (2 M) is of great significance in NiO applications such as spin valves and next-generation magnetic random access memories (MRAM). We investigated the phonon modes and antiferromagnetically ordered states of NiO nanoparticles prepared by empirically controlled measurements. An intensity enhancement of the 2 M mode was observed by Raman spectroscopy as the NiO nanoparticles were vacuum annealed at 650 ℃. The increased 2 M peak intensity in NiO nanoparticles is explained by the local symmetry conversions from NiO ₅ to NiO ₆ configurations due to the oxygen redistribution during the vacuum annealing. The change of the splitting of anisotropic transverse optical (TO) phonon with different oxygen contents was also revealed by the Raman spectroscopy. We have shown that the changes in the oxygen environment underlie both the change in the 2 M intensity and the splitting of TO phonon in the NiO nanoparticles. Our work offers an efficient avenue to strengthen the AFM ordering and emphasizes the effect of vacuum annealing of the NiO nanoparticles, opening the interesting possibility of individual parameter control in practical applications.
Competing Interests: Declaration of Competing Interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
(Copyright © 2023 Elsevier B.V. All rights reserved.)