Use of final irrigant potassium titanyl phosphate laser; Sapindus Mukorossi and Fotoenticine on the bond values of zirconia post-to-canal dentin.

Aims: Assessment of the efficacy of final root canal irrigants Sapindus mukorossi (SM), Potassium titanyl phosphate laser (KTPL), and Fotoenticine (FTC) on the push-out bond strength (PBS) of zirconia post.
Materials and Methods: The root canal procedure was initiated using the 10 K file and the working length was determined on single-rooted human premolar teeth after decoration. The canals were then enlarged using ProTaper universal system and filled using single cone gutta-percha (GP) and AH Plus resin sealer. Post space was prepared by removing 10 mm of GP from the canal. All the teeth were then allocated into four groups based on the final irrigating regime used (n = 10) Group 1: 5.25% NaOCl+17% EDTA, Group 2: 5.25% NaOCl + KTPL, Group 3: 5.25% NaOCl + FTC and Group 4: 5.25% NaOCl+ SM. Zirconia posts were cemented in the canal space. The specimens were sectioned and implanted in auto-polymerizing acrylic resin. A universal testing machine and stereomicroscope at 40x magnification were used for PBS and failure mode analysis. ANOVA and Tukey post hoc test were used to make group comparisons(p = 0.05).
Results: Group 4 (5.25% NaOCl+ SM) coronal section displayed the highest PBS (9.29±0.24 MPa). However, group 3 (5.25% NaOCl+ FTC) apical third (4.08±0.14 MPa) showed the lowest bond values. Group 2 (5.25% NaOCl+ KTP laser) and Group 3 at all three-thirds unveiled no significant difference in PBS(p>0.05). However, Group 1 (5.25% NaOCl+17%EDTA) and Group 4 displayed comparable outcomes of bond strength(p>0.05) CONCLUSION: Sapindus mukorossi has the ability to be used as a final root canal irrigant alternative to EDTA. However, future studies are still required to conclude the outcomes of existing research.
(Copyright © 2023. Published by Elsevier B.V.)