Effect of preheating and ultrasound application of resin-based luting agents on the failure load of a lithium disilicate glass-ceramic.

Purpose: To assess the effect of preheating resin-based materials and ultrasound application on the failure load of a lithium disilicate glass-ceramic.
Materials and Methods: Ninety ceramic specimens were produced (14×12×1.0 mm) and divided into 9 groups (n = 10) to be bonded to a dentin analog (Nema G10) with light-cured luting agent (LC), flowable resin composite (FL), and supra-nano filled resin composite (SN), as follows: LC/R - LC at room temperature; LC/P - preheated LC; LC/P/U - preheated LC and Ultrasound; FL/R - FL at room temperature; FL/P - preheated FL; FL/P/U - preheated FL and Ultrasound; SN/R - SN at room temperature; SN/P - preheated SN; SN/P/U - preheated SN and Ultrasound. The failure load test was performed in a universal testing machine with the aid of acoustic detection. The data was analyzed with two-way ANOVA (for failure load) and Weibull statistics (Weibull modulus - m and characteristic strength, based on 95% confidence intervals - CI).
Results: The analyses of failure load revealed no statistically significant difference among groups considering the type of luting agent (P = 0.075; F = 2,673), the application method (P = 0.772; F = 2,259), and the interaction between them (P = 0.297; F = 1,248). The characteristic strength did not show differences among groups (95% CI). The m, which indicates structural reliability, showed lower values for SN/P/U and SN/P, with a difference from other selected groups (95% CI).
Conclusion: Preheating of resin-based materials and ultrasound application did not affect the failure load of lithium disilicate glass-ceramic. Lower reliability was observed with supra-nano filled resin composite.
(© 2023 by the American College of Prosthodontists.)