Effect of molecular weight of PEI on the strength and hydrophobic performance of fiber-based papers via PEI-KH560 surface sizing.

In recent years, researchers have put much attention on the improvements and upgrades of novel wet strength agent in the papermaking fields, especially in the usage of household paper. Herein, PEI _M -KH560 by polyethyleneimine (PEI) and γ-glycidyl ether propyl trimethoxysilane (KH560) was synthesized with five molecular weights (Mw) of PEI at 600, 1800, 10,000, 70,000 and 750,000. Results showed that the molecular weight greatly influenced the physicochemical properties of PEI-KH560, such as the size and thermal stability. The intrinsic cationic charge of PEI-KH560 provided the bonding sites with the paper fibers, forming strengthened fiber-fiber joints. It was shown that the dry, wet strength and hydrophobicity of cellulosic paper sheets were obviously improved. When the m (PEI):m(KH560) is 1:2, the strength of papers after sizing by Mw of PEI at 600 and 1800 is the most obvious, with the dry strength increased by 227.9 % and 187.5 %, and the wet strength increased by 183.8 % and 207.8 %, respectively. The maximum hydrophobicity was found at the PEI ₁₈₀₀ -KH560 with the contact angle value of 130.6°. The resultant environmental-friendly agent (PEI-KH560) obtained in this work provides valuable significance for the preparation of household and food packaging paper.
Competing Interests: Declaration of competing interest The authors declare that they have no known competing interests or personal relationships that could have appeared to influence the work reported in this paper.
(Copyright © 2024 Elsevier B.V. All rights reserved.)