Treatment outcomes and prognostic factors of the apical barrier technique with premixed calcium silicate-based putty in necrotic permanent teeth with open apices: a retrospective cohort study with up to six years follow-up.

Objectives: To evaluate treatment outcomes of the apical barrier technique with premixed calcium silicate-based putty for treating necrotic permanent teeth with open apices and to identify prognostic factors.
Materials and Methods: Permanent teeth with necrotic pulps and open apices treated by the apical barrier technique with premixed calcium silicate-based putty, with a minimum follow-up of 12 months, were included. Treatment outcomes were based on clinical signs, symptoms, and radiographic evaluation. The treatment outcome was dichotomized into success or failure according to strict and loose criteria. The chi-square test (or Fisher's exact test) and multiple logistic regression analysis were used to evaluate possible prognostic factors associated with treatment outcomes.
Results: Seventy-four teeth with a follow-up time of 12-72 months (mean, 25.74 ± 14.36 months) were included in the final evaluation. The success rate was 97.30% using the loose criteria and 66.22% using the strict criteria. Multiple logistic regression analysis indicated that the size of pre-operative periapical lesion (≥ 5 mm) (odds ratio [OR]: 18.96; P = 0.0153) and root canal underfilling (OR: 8.341; P = 0.0448) were significant predictors for treatment failure under the strict criteria.
Conclusion: The apical barrier technique with premixed calcium silicate-based putty is a highly successful procedure for treating necrotic permanent teeth with open apices after an observation period of up to 6 years. Treatment success under the strict criteria is primarily affected by the size of the pre-operative periapical lesion and the apical extent of root-filling.
Clinical Relevance: Careful case selection and ensuring adequate root filling quality are essential to the successful outcome of the apical barrier technique with premixed calcium silicate-based putty.