Microstructural change due to isochronal annealing in severely plastic-deformed commercial purity aluminium.
- Source :
- Philosophical Magazine; Apr2015, Vol. 95 Issue 11, p1139-1149, 11p
- Publication Year :
- 2015
-
Abstract
- Microstructural changes, such as the density of grain boundary (GB) and dislocation density, due to isochronal annealing in severely plastic-deformed commercial purity aluminium up to 523 K was evaluated using electrical resistivity measurements and scanning transmission electron microscopy. Eventually, the GB density decreases from about 7.2  ×  106to about 2  ×  106 m−1, whilst the dislocation density decreases from an initial value of around 1.3  ×  1014 m−2down to around 4  ×  1013 m−2. [ABSTRACT FROM PUBLISHER]
Details
- Language :
- English
- ISSN :
- 14786435
- Volume :
- 95
- Issue :
- 11
- Database :
- Complementary Index
- Journal :
- Philosophical Magazine
- Publication Type :
- Academic Journal
- Accession number :
- 102014589
- Full Text :
- https://doi.org/10.1080/14786435.2015.1021400