Study on the properties of a nanocrystal and polymer composite PbTiO3/PEK-c film with optical anisotropy.

Composite thin films of PbTiO₃ nanocrystals and PEK-c polymer for applications in nonlinear optical devices were prepared by spin coating. The size of PbTiO₃ nanocrystals was estimated to be 30–40 nm. The microstructure of PbTiO₃/PEK-c composite polymer film before and after poling was analyzed by X-ray diffraction, which show that this film is c axis-orientated. The poled composite film displayed the refractive index anisotropy. In this sample the TE- and TM-indices differences are found to be 0.02945 for 633 nm and 0.03915 for 414 nm. The electro-optic coefficient γ₃₃ of poled composite film was measured to be 12.89 pm V^-1 at 633 nm by the transmission technique. The dielectric constant ε of it at 100 KHz under room temperature was determined to be 7.32. The figure of merit F₂ was estimated to be 492. In addition, a relaxation process was observed in the time range of 28 days and the relaxation time constant was calculated to be 2393 min. [ABSTRACT FROM AUTHOR]