Combustion Synthesis of High Density ZrN/ZrSi 2 Composite: Influence of ZrO 2 Addition on the Microstructure and Mechanical Properties.

In this study, a high-density ZrN/ZrSi₂ composite reinforced with ZrO₂ as an inert phase was synthesized under vacuum starting with a Zr-Si₄N₃-ZrO₂ blend using combustion-synthesis methodology accompanied by compaction. The effects of ZrO₂ additions (10–30 wt%) and compression loads (117–327 MPa) on the microstructure, porosity and hardness of the samples were studied. The process was monitored using XRD, SEM, EDS, porosity, density and hardness measurements. Thermodynamic calculations of the effect of ZrO₂ addition on the combustion reaction were performed including the calculation of the adiabatic temperatures and the estimation of the fractions of the liquid phase. The addition of up to 20 wt% ZrO₂ improved the hardness and reduced the porosity of the samples. Using 20 wt% ZrO₂, the sample porosity was reduced to 1.66 vol%, and the sample hardness was improved to 1165 ± 40.5 HV at 234 MPa. [ABSTRACT FROM AUTHOR]