Microstructure and Corrosion Resistance of Fusion Welding Zone for Duplextubes Welded with Q345R Tube Sheet under Different Welding Currents.

Duplextubes are widely used in oil and gas storage and transportation, the nuclear industry, and other fields, but the welding quality of metals is an important factor affecting the use of equipment. In order to study the welding quality of S10C steel/Incoloy 825 duplextubes and Q345R tube sheet based on gas tungsten arc welding technology with a filler of ER50-6 carbon steel welding wire, the microstructure and grain size of fusion welding zone of duplextubes and tube sheet under welding currents of 150 A, 160 A, and 170 A were studied by optical microscopy and scanning electron microscopy. At the same time, the corrosion behavior of fusion welding zone after the welding was investigated in 3.5 wt.% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy. The results show that the metallurgical structure of the fusion welding zone was mainly composed of δ-ferrite and retained austenite. The grain size in the fusion welding zone increased with the increase of the welding current. The corrosion resistance of the fusion welding zone welded with a high welding current of 170 A was better than that with low welding currents. However, the pitting corrosion resistance of fusion welding zone with the lowest welding current of 150 A was better than that with high welding currents. This study can provide a preliminary exploration for the manufacture and applicability of duplextubes air coolers. [ABSTRACT FROM AUTHOR]