Microstructural Evolution of Shear Localization in High-Speed Cutting of CoCrFeMnNi High-Entropy Alloy.
- Source :
- Metals (2075-4701); Apr2023, Vol. 13 Issue 4, p647, 9p
- Publication Year :
- 2023
-
Abstract
- Shear localization is one of the most important failure mechanisms subjected to high-strain-rate deformation and has significant effects on the process, plastic deformation, and catastrophic failure of a material. Shear localization was observed in serrated chips produced during the high-speed cutting of the CoCrFeMnNi high-entropy alloy. Electron backscatter diffraction was performed to systematically investigate microstructural evolution during shear banding. The elongation and subdivision of the narrow grains were observed in the areas adjacent to the shear band. The microstructure inside the shear band was found to be composed of equiaxed ultrafine grains. The results reveal that grain subdivision and dynamic recrystallization might have significant roles in the microstructural evolution of shear bands. These results offer key insights into our understanding of shear localization and high-speed machining behavior for high entropy alloys. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 20754701
- Volume :
- 13
- Issue :
- 4
- Database :
- Complementary Index
- Journal :
- Metals (2075-4701)
- Publication Type :
- Academic Journal
- Accession number :
- 163434174
- Full Text :
- https://doi.org/10.3390/met13040647