Characterization and High-Temperature Oxidation Behavior of Ni–20Cr Deposits Fabricated by Cold Spray-Based Additive Manufacturing.

Hot corrosion is a critical problem in a wide range of high-temperature applications. Ni–20Cr alloy is frequently used in such applications owing to its good hot-corrosion resistance. In the current work, thick Ni–20Cr plates in a thickness range of 6–10 mm were fabricated using cold spray-based additive manufacturing (CSAM). High-pressure cold spraying was used with nitrogen as the propellant gas. Pre- (substrate heating, SH) and post-heat treatments (hot isostatic pressing, HIP) were also performed to comprehend the changes in the deposit properties. The deposits were subjected to microstructural and mechanical characterization to explore the potential of cold spraying for CSAM of Ni–20Cr standalone products. The cold-sprayed plates were successfully developed without any oxide formation. HIP treatment was found to be useful to reduce porosity. The cold-sprayed substrate-heated Ni–20Cr deposits exhibited excellent oxidation resistance at a high temperature of 900 °C. [ABSTRACT FROM AUTHOR]