Circular Production, Designing, and Mechanical Testing of Polypropylene-Based Reinforced Composite Materials: Statistical Analysis for Potential Automotive and Nuclear Applications.

The circularity of polymer waste is an emerging field of research in Europe. In the present research, the thermal, surface, mechanical, and tribological properties of polypropylene (PP)-based composite produced by injection molding were studied. The pure PP matrix was reinforced with 10, 30, and 40% wt. of pure cotton, synthetic polyester, and polyethylene terephthalate post-consumer fibers using a combination of direct extrusion and injection molding techniques. Results indicate that PP-PCPESF-10% wt. exhibits the highest value of tensile strength (29 MPa). However, the values of tensile and flexural strain were lowered with an increase in fiber content due to the presence of micro-defects. Similarly, the values of modulus of elasticity, flexural modulus, flexural strength, and impact energy were enhanced due to an increase in the amount of fiber. The PP-PCCF-40% wt. shows the highest values of flexural constant (2780 MPa) and strength (57 MPa). Additionally, the increase in fiber loadings is directly proportional to the creation of micro-defects, surface roughness, abrasive wear, coefficient of friction, and erosive wear. The lowest average absolute arithmetic surface roughness value (R_a) of PP and PP-PCCF, 10% wt., were 0.19 µm and 0.28 µm. The lowest abrasive wear value of 3.09 × 10⁻⁶ mm³/Nm was found for pure PP. The erosive wear value (35 mm³/kg) of PP-PCCF 40% wt. composite material was 2 to 17 times higher than all other composite materials. Finally, the single-step analysis of variance predicts reasonable results in terms of the p-values of each composite material for commercial applications. [ABSTRACT FROM AUTHOR]