Comparative evaluation of cyclic fatigue resistance of thermomechanically treated NiTi rotary instruments in simulated curved canals with two different radii of curvature: An in vitro Study.

Background: This study aimed to compare the effect of heat treatment on the cyclic fatigue resistance of three different nickel-titanium rotary file systems: TruNatomy, HyFlex CM, and NeoEndo flex in simulated curved canals at two different radii of curvatures. Materials and Methods: A total of 60 NiTi rotary files of three types were used, and the samples were divided into three groups TruNatomy, HyFlex CM, and NeoEndo flex. All the instruments were subjected to cyclic fatigue testing using a stainless steel custom-made canal model with a 60° angle of curvature and two radii of curvature 5 mm and 3 mm; the number of cycles to fracture and length of the fractured segment was measured. The separated instruments were subjected to fractographic analysis under scanning electron microscope. Results: The number of cycles to failure to fracture a file at a 3 mm radius of curvature is significantly less as compared to a 5 mm radius of curvature (HCM > TRN > NE). Conclusion: Within the limitation of the present study, there was a positive correlation between the radius of curvature and fatigue life of NiTi files. [ABSTRACT FROM AUTHOR]