Synergistic Effect of B 4 C and Multi-Walled CNT on Enhancing the Tribological Performance of Aluminum A383 Hybrid Composites.

The requirement for high-performance and energy-saving materials motivated the researchers to develop novel composite materials. This investigation focuses on utilizing aluminum alloy (A383) as the matrix material to produce hybrid metal matrix composites (HMMCs) incorporating boron carbide (B₄C) and multi-walled carbon nanotube (MWCNT) through a cost-effective stir casting technique. The synthesis of HMMCs involved varying the weight fractions of B₄C (2%, 4%, and 6%) and MWCNT (0.5%, 1%, and 1.5%). The metallographic study was carried out by field emission scanning electron microscopy (FESEM) mapped with EDS analysis. The results indicated a uniform dispersion and robust interfacial interaction between aluminum and the reinforced particles, significantly enhancing the mechanical properties. Micro-hardness and wear characteristics of the fabricated HMMCs were investigated using Vickers microhardness testing and the pin-on-disc tribometer setup. The disc is made of hardened chromium alloy EN 31 steel of hardness 62 HRC. The applied load was varied as 10N, 20N, 30N with a constant sliding speed of 1.5 m/s for different sliding distances. The micro-hardness value of composites reinforced with 1.5 wt% MWCNT and 6 wt% B₄C improved by 61% compared to the base alloy. Additionally, the wear resistance of the composite material improved with increasing reinforcement content. Incorporating 1.5% CNT and 6% B₄C as reinforcements results in the composite experiencing about a 40% reduction in wear loss compared to the unreinforced aluminum alloy matrix. Furthermore, the volumetric wear loss of the HMMCs was critically analyzed with respect to different applied loads and sliding distances. This research underscores the positive impact of varying the reinforcement content on the mechanical and wear properties of aluminum alloy-based hybrid metal matrix composites. [ABSTRACT FROM AUTHOR]