Magnetic properties of Fe0.4Mn0.6/Co2FeAl bilayers grown on GaAs by molecular-beam epitaxy.

Polycrystalline Fe0.4Mn0.6 layers with the different thickness are deposited on 4-nm-thick single-crystalline Co2FeAl layers, which are grown on GaAs (001) substrates at room temperature by molecular-beam epitaxy. Both the exchange bias and the in-plane magnetic anisotropies of the bilayers are strongly dependent on the thickness of the Fe0.4Mn0.6 layer. The former is described using a granular level model. A modified Stoner-Wohlfarth model is used to explain the in-plane magnetic anisotropies observed at 5 K, while one possible reason for the magnetic anisotropies measured at 300 K is the complex interfacial magnetic properties proved by x-ray magnetic circular dichroism measurements. [ABSTRACT FROM AUTHOR]