Plasma homo- and copolymerizations of tetrafluoroethylene and chlorotrifluoroethylene.

The plasma homo- and copolymerizations of tetrafluoroethylene (TFE) and chlorotrifluoroethylene (CTFE) in a capacitively coupled tubular reactor (TR) with external electrodes were studied by means of microgravimetry and FT-IR and XPS analyses. The deposition rates for CTFE/TFE plasma copolymers, as well as the ratios of IR absorbances at 1180 and 1225 cm, and the XPS-derived Cl/C and F/C ratios, varied regularly with mol % CTFE in the feed, all of which results were dependent upon the rf power at which the plasma copolymerizations were conducted. The deposition rates for the plasma homopolymers of TFE (PPTFE) and CTFE (PPTCFE) depended markedly on rf power ( W) and monomer molar flow rate ( F). The F/C ratio for PPTFE was nearly independent of the composite parameter, W/FM (where M is the monomer molecular weight), while for PPCTFE, the F/C ratio decreased significantly and the Cl/C ratio increased slightly with increase in W/FM. The percentage of carbon as CF was 20-24% in PPTFE and 7-14% in PPCTFE. Plots of deposition rate versus W/FM for PPTFE and PPCTFE obtained in a TR differed considerably from corresponding plots in the literature for the same homopolymers prepared in a glass-cross or bell-jar reactor. [ABSTRACT FROM AUTHOR]