Aligned and exchange-coupled L10 (Fe,Co)Pt-based magnetic films.
- Source :
- Journal of Applied Physics; Apr2012, Vol. 111 Issue 7, p07B537-07B537-3, 1p
- Publication Year :
- 2012
-
Abstract
- Films of aligned L10-structure (Fe,Co)Pt with fcc Fe(Co,Pt) are synthesized by co-sputtering Fe, Co, and Pt on an (001) MgO substrate with in situ heating at 830 °C. The nanostructures and magnetic properties of the films are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and superconducting quantum interference device (SQUID). The compositions of the samples (Fe,Co)xPt1-x are designed to maintain an atomic Fe: Co ratio of 65: 35 while increasing the Fe,Co content in each successive sample. In samples with low Fe and Co concentration, the XRD patterns exhibit three strong peaks, namely L10 (Fe,Co)Pt (001), L10 (Fe,Co)Pt (002), and MgO (002). A fourth peak is observed in samples with high Fe and Co concentration and identified as fcc (002). The XRD patterns confirm the formation of L10-ordered (Fe,Co)Pt and its epitaxial growth on MgO. TEM shows that the (Fe,Co)Pt films form isolated magnetic grains of about 100 nm in diameter. Hysteresis-loop measurements show that the increase of the Fe,Co concentration from 57.3 to 68.3 at % enhances the saturation magnetization Ms from 1245 emu/cm3 to 1416 emu/cm3, and the coercivity decreases from 32 kOe to 8.9 kOe. The nominal maximum energy product per grain is 64 MGOe. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 00218979
- Volume :
- 111
- Issue :
- 7
- Database :
- Complementary Index
- Journal :
- Journal of Applied Physics
- Publication Type :
- Academic Journal
- Accession number :
- 74279592
- Full Text :
- https://doi.org/10.1063/1.3679099