Magnetism and electron transport of MnyGa (1 < y < 2) nanostructures.
- Source :
- Journal of Applied Physics; Jul2013, Vol. 114 Issue 1, p013906-013906-5, 1p, 1 Black and White Photograph, 1 Chart, 4 Graphs
- Publication Year :
- 2013
-
Abstract
- Nanostructured MnyGa ribbons with varying Mn concentrations including Mn1.2Ga, Mn1.4Ga, Mn1.6Ga, and Mn1.9Ga were prepared using arc-melting and melt-spinning followed by a heat treatment. Our experimental investigation of the nanostructured ribbons shows that the material with y = 1.2, 1.4, and 1.6 prefers the tetragonal L10 structure and that with y = 1.9 prefers the D022 structure. We have found a maximum saturation magnetization of 621 emu/cm3 in Mn1.2Ga which decreases monotonically to 300 emu/cm3 as y reaches 1.9. Although both the L10- and D022-MnyGa samples show a high Curie temperature (Tc) well above room temperature, the value of Tc decreases almost linearly from 702 K for Mn1.9Ga to 551 K for Mn1.2Ga. All the ribbons are metallic between 2 K and 300 K but the Mn1.2Ga also shows a resistance minimum near 15 K. The observed magnetic properties of the MnyGa ribbons are consistent with the competing ferromagnetic coupling between Mn moments in the regular L10-MnGa lattice sites and antiferromagnetic coupling with excess Mn moments occupying Ga sites. [ABSTRACT FROM AUTHOR]
- Subjects :
- NANOSTRUCTURES
MAGNETISM
ELECTRON transport
MANGANESE compounds
PHYSICS research
Subjects
Details
- Language :
- English
- ISSN :
- 00218979
- Volume :
- 114
- Issue :
- 1
- Database :
- Complementary Index
- Journal :
- Journal of Applied Physics
- Publication Type :
- Academic Journal
- Accession number :
- 88899419
- Full Text :
- https://doi.org/10.1063/1.4812561