Fabrication of chitosan/silica hybrid coating on AZ31 Mg alloy for orthopaedic applications.

Biocompatible conversion of chitosan and chitosan/silica hybrid coating were prepared to enhance the biocompatibility and corrosion resistance of biodegradable AZ31 Mg alloy. The coatings were optimized and analysed with potentiodynamic polarization, SEM, ATR-IR and XPS studies. Potentiodynamic polarization studies, revealed that the coatings exhibited high corrosion resistance. The surface morphology of the Ch-3/Si coating showed small globular rough structure. The presence of functional groups was confirmed by ATR-IR. For a better understanding of chitosan/silica hybrid coating, the chemical states were examined by XPS studies. The in-vitro bioactivity of the coated samples was evaluated in Earle's solution, which formed a dense layer of coral-like structure and calcium-deficient apatite with less stoichiometric ratio than the hydroxyapatite. In-vitro cell culture studies exhibited a good cell proliferation rate and the fabricated Ch-3/Si coating was found to be non-hemolytic. The bacterial studies proved that Ch-3/Si coating possessed inherent antibacterial activity. [ABSTRACT FROM AUTHOR]