Preparation, structures and photoluminescent enhancement effect of PbWO4–TiO2 composite nanofilms

Abstract: A novel route for preparing PbWO₄–TiO₂ nanofilms on a glass substrate is firstly proposed. The collodion is used as a dispersant and film-forming agent. The nanofilms are characterized through SEM, XRD, TG/DTA, PL and IR, respectively. The results of XRD indicate PbWO₄ particles with tetragonal scheelite structure and TiO₂ particles with Anatase phase, and SEM shows they are well dispersed in the substrate. Compared with nanoparticles, when TiO₂ nanoparticles are added in 5% ratio, the PL intensities at 395 nm of PbWO₄ nanofilms are enhanced obviously. IR spectrum reveals a large absorption band between 750 and 870 cm⁻¹, which is the W–O stretching vibration in WO₄ tetrahedron.