Preparation of Lead Lanthanum Zirconate Titanate (PLZT, (Pb,La)(Zr,Ti)O3) Fibers by Sol-Gel Method
- Source :
- Journal of the American Ceramic Society; May 1998, Vol. 81 Issue: 5 p1189-1196, 8p
- Publication Year :
- 1998
-
Abstract
- Lead lanthanum zirconate titanate (PLZT, (Pb,La)(Zr,-Ti)O3) ceramic fibers were prepared by the sol-gel method from a solution of lead acetate trihydrate, lanthanum isopropoxide, zirconium n-propoxide, and titanium isopropoxide that contained 2-methoxyethanol as the solvent. The sols obtained from the solution were concentrated at 156°-174°C for 2 h. Concentration at higher temperatures resulted in more-viscous sols of higher specific gravities. The concentration resulted in the formation of spinnable sols, which had viscosities >105mPas and exhibited Newtonian flow properties. These spinnable sols were formed to be so stable that no change in viscosity and spinnability was observed for more than three months when stored in a sealed container at room temperature. Gel-to-ceramic fiber conversion was investigated by means of X-ray diffractometry, infrared spectroscopy, and thermal analysis. Single-phase perovskite PLZT ceramic fibers 5-200 ?m in diameter and >20 cm in length were obtained. Scanning electron microscopy (SEM) observation and Brunauer-Emmett-Teller (BET) measurement showed that heat treatment of the fibers at a lower rate resulted in the formation of fibers of denser microstructure. Although the SEM image of the cross section of the fibers revealed a relatively dense microstructure and a laser beam could be transmitted through a fiber 6 mm in length, BET measurement of the fibers indicated that the fibers had more than a few percent of open porosities, and scattering of light was observed in the laser-beam guiding test.
Details
- Language :
- English
- ISSN :
- 00027820 and 15512916
- Volume :
- 81
- Issue :
- 5
- Database :
- Supplemental Index
- Journal :
- Journal of the American Ceramic Society
- Publication Type :
- Periodical
- Accession number :
- ejs21397925
- Full Text :
- https://doi.org/10.1111/j.1151-2916.1998.tb02467.x