Preparation of Crosslinked High-density Polyethylene Foam Using Supercritical CO2as Blowing Agent

Different content of dicumyl peroxide (DCP) acting as a crosslinking agent was mixed with high-density polyethylene (HDPE) in a Haake internal mixer to improve the viscoelasticity and foamability of HDPE. The crosslinked HDPE samples were foamed in a high pressure stainless steel autoclave using CO2as the physical blowing agent. The molecular weight, crystallization behavior and rheological properties of various HDPE samples were examined by gel permeation chromatography, differential scanning calorimetry, rotational rheometer, and torque rheometer, respectively. The foaming properties of various samples were characterized by scanning electron microscope and densimeter. It was found that with the increasing content of DCP, the molecular weight, crystallization temperature, complex viscosity, and storage modulus of HDPE increased and the crystallization degree of HDPE decreased. When 0.2 phr of DCP was introduced into HDPE, the expansion volume ratio of HDPE showed the highest value, which could be more than 7 times.