Rapid Preparation of TiO2–xand Its Photocatalytic Oxidation for Arsenic Adsorption under Visible Light

A rapid preparation method of TiO2–xby thermal treatment using H2TiO3as the precursor was proposed compared with the static hydrogenation thermal treatment process. Its adsorption properties of arsenic under visible light were explored and investigated as well. Various colors of TiO2–xwere prepared and characterized via XRD, TEM, BET, and so on. The results indicate that the method of rapid preparation is feasible. The TiO2–xexhibits a larger particle size that varied from 10 nm to 2 μm, and deeper color products were obtained as the treatment temperature increased from 600 to 900 °C. Light yellow TiO2–xwas prepared after increasing the temperature from 600 to 900 °C, Ti4O7and Ti6O11with a dark color were formed under a H2atmosphere at 1500 °C. The arsenic adsorption performances of some samples under visible light were tested, and reveal a high efficiency of TiO2–xin the photocatalytic oxidation arsenic adsorption under visible light, the conversion ratio of As(III) photocatalytic oxidation fluctuates around 2.85 mgAsg–1h–1. In the absence of visible light, the adsorption capacities for As(III) and As(V) are 3.7 and 42.7 mg/g, respectively, at pH = 3. Under visible light condition, the adsorption capacity of As(III) increases sharply to 15.6 mg/g, which provides the foundation for a new application of TiO2–xin the field of arsenic adsorption.