Cr-Substituted SrCoO3-δPerovskite with Abundant Oxygen Vacancies for High-Energy and Durable Low-Temperature Antifreezing Flexible Supercapacitor
- Source :
- Inorganic Chemistry; July 2024, Vol. 63 Issue: 29 p13755-13765, 11p
- Publication Year :
- 2024
-
Abstract
- Developing high-performance electrodes for flexible antifreezing energy storage devices has been a significant challenge with the increasing demand for portable components. In this work, Cr-substituted SrCoO3-δperovskites were first proposed as potential low-temperature supercapacitor electrode materials. The high-valence Cr6+([Ne]3s23p6) substitution favors a high-spin state of Co ions with enhanced electronic repulsion effect, ultimately forming a stable cubic structure with high conductivity. Accordingly, the modification strategies of SrCoO3through the p6 configuration cation substitution have been improved. As a result, the asymmetric SrCo0.95Cr0.05O3-δ@CC//PPy@CC device exhibited a high energy density of 44.90 Wh kg–1at 902.01 W kg–1and maintained a 95.8% specific capacitance after 10,000 cycles, demonstrating an ultralong cyclic stability. The dramatically improved electrochemical performance was attributed to the stabilized crystal structure, increased oxygen vacancy, and accelerated oxygen diffusion rate. Furthermore, a quasi-solid-state supercapacitor with ethylene glycol (EG)-modified KOH/PVA organohydrogel electrolyte was developed through an advance in situ-integrated strategy. After bending at 180° for 1000 cycles, only a 9.7% capacity decay was observed. Even under −40 °C, the supercapacitor has a large energy density of 46.94 μWh cm–2. The present work represents the initial investigation into utilizing perovskite materials for antifreezing energy storage device, thereby confirming their potential application as low-temperature electronic components.
Details
- Language :
- English
- ISSN :
- 00201669 and 1520510X
- Volume :
- 63
- Issue :
- 29
- Database :
- Supplemental Index
- Journal :
- Inorganic Chemistry
- Publication Type :
- Periodical
- Accession number :
- ejs66881058
- Full Text :
- https://doi.org/10.1021/acs.inorgchem.4c02115