Tribological Properties of Al2O3/CuCrZr Composites

Al2O3 particles reinforced Cu–Cr–Zr alloy matrix composite was fabricated through a powder metallurgy plus hot extrusion process by using the water atomization Cu–Cr–Zr powder as raw material. The effect of aging treatment on the tribological behavior of the composite was investigated. Experimental results show that tiny coherent precipitated phases were formed in the matrix after proper aging treatment and therefore good combination properties could be obtained. The wear rates of the Al2O3/CuCrZr composite and its matrix alloy were obviously influenced by the aging treatment, wherein the best wear resistance was reached at the aging temperature corresponding to the highest Vickers hardness. The major reason was that the depth of plastic deformation in the subsurface region was dramatically decreased due to the improvement of mechanical properties of the matrix, and therefore adhesion induced surface materials loss could be markedly alleviated. By comparing with the SiC20 vol%/Cu composite, it is indicated that the Al2O3/CuCrZr composite exhibited much better wear resistance as well as higher electrical conductivity.