Direct Observations of Grain Boundary Phenomena during Indentation of Al and Al-Mg Thin Films

The deformation behavior of Al and Al-Mg thin films has been studied with the unique experimental approach of in-situ nanoindentation in a transmission electron microscope. This paper concentrates on the role of solute Mg additions in the transfer of plasticity across grain boundaries. The investigated Al alloys were deposited onto a Si substrate as thin films with a thickness of 200–300 nm and Mg concentrations of 0, 1.1, 1.8, 2.6 and 5.0 wt% Mg. The results show that in the Al-Mg alloys, the solutes effectively pin high-angle grain boundaries, while in pure Al considerable grain boundary motion is observed at room temperature. The mobility of low-angle grain boundaries is however not affected by the presence of Mg. In addition, Mg was observed to affect dislocation dynamics in the matrix.