Ternary rare-earth zinc arsenides REZn2As3 (RE=La–Pr) containing defect fluorite-type slabs

The ternary rare-earth zinc arsenides RE Zn 2 As 3 ( RE =La–Pr) have been prepared by reactions of the elements at 800 °C. They adopt new tetragonal structure types, with the La member (space group I 4/ mmm , Z =4, a =4.1133(2) A, c =32.1246(14) A) differing from the Ce and Pr members (space group P 4/ nmm , Z =2, a =4.0804(6)–4.0534(12) A, c =16.089(5)–16.059(10) A, respectively) in the disposition of RE -centred square antiprisms on opposite sides of square As nets. The structures contain thick anionic slabs, built from edge-sharing ZnAs 4 tetrahedra, that can be considered either as stackings of three PbO-type layers or as fragments of the fluorite-type structure. These slabs are deficient in Zn and are reminiscent of the same features in binary arsenide Zn 3 As 2 . LaZn 2 As 3 exhibits temperature-independent paramagnetism whereas CeZn 2 As 3 follows modified Curie–Weiss behavior consistent with Ce 3+ species but with no occurrence of long-range ordering.