Microstructure evolution of semi-solid SiCp/AZ91D nanocomposite during isothermal heat treatment process

The microstructure evolution of semi-solid SiCp/AZ91D nanocomposite during isothermal heat treatment process in the mushy-zone was investigated. The results indicate that the nano-size SiC particles in composite are distributed uniformly and the grains are refined significantly by the addition of nano-size SiC particles. The semi-solid microstructure evolution experiences four stages during isothermal heat treatment process: the initial coarsening, structural separation, spheroidization and final coarsening. The grain size of the primary α-Mg phase decreases with the increasing of holding temperature. With the prolongation of holding time, the grain size of the primary α-Mg phase decreases at first and then increases. The optimum isothermal heat treatment parameter is 575℃ for 30min, under which the average grain diameter is 58μm and shape factor is 1.25.