MONOCLINIC-ORTHORHOMBIC PHASE TRANSITION IN THE METASTABLE BiCr1-xScxO3 (x=0, 0.1) PEROVSKITES

MONOCLINICORTHORHOMBIC PHASE TRANSITION IN THE METASTABLE BiCr1xScxO3 (x0, 0.1) PEROVSKITES Cardoso J.P.1, Delmonte D.2, Gilioli E.2, Shvartsman V.V.3, Vieira J.M.1, Salak A.N.1 1Department of Materials and Ceramics Engineering and CICECO Aveiro Institute of Materials, University of Aveiro, Aveiro, Portugal, joaopcardosoua.pt 2Institute of Materials for Electronics and Magnetism, Parma, Italy 3Institute for Materials Science and CENIDE Center for Nanointegration DuisburgEssen, University of DuisburgEssen, Essen, Germany Here we report on a comparative study of reversible phase transition from the monoclinic C2/c phase (resultant from highpressure synthesis) to the nonpolar orthorhombic Pnma phase in BiCrO3 and BiCr0.9Sc0.1O3. Due to a considerable size difference between Cr3 by Sc3, 10 mol substitution of chromium by scandium was expected to result in structural changes without destroying the longrange magnetic order. Здесь мы сообщаем о сравнительном исследовании обратимого фазового перехода из моноклинной фазы C2/c (полученной в результате синтеза под высоким давлением) в неполярную орторомбическую фазу Pnma в BiCrO3 и BiCr0.9Sc0.1O3. Изза значительной разницы в размерах между Cr3 Sc3 , ожидается, что 10 ное замещение хрома скандием приведет к структурным изменениям без разрушения дальнего магнитного порядка.