Kinetics of recrystallization and grain growth in an ultra-fine grained CoCrFeNiMn-type high-entropy alloy

A novel high entropy alloy based on the CoCrFeMnNi system with substantial amounts of Al and C was studied. After cold rolling and annealing at 973-1273 K a duplex ultra-fine grained structure composed of the recrystallized fcc grains and M23C6 and B2 particles was produced. Analysis of the coarsening behavior of grains and particles growth suggested that kinetics of both was controlled by volume diffusion. The apparent activation energy of structure coarsening during recrystallization was evaluated.