Mössbauer studies of FeBe, FeNb, FeRu, FeTe, and FeIr alloys

The isomer shifts, quadrupole splittings, and magnetic hyperfine splittings of iron in α-Fe–Be: FeBe5, α-Fe–Nb, γ-Fe–Nb, α-Fe–Ru, γ-Fe–Ru, FeTe2, α-Fe–Ir, and γ-Fe–Ir alloys are measured using the Mossbauer effect. Some of these studies were carried out as a function of temperature in the temperature range 60 to 300 °K. All of the systems except FeBe5 and γ-Fe–Ir are studied for the first time. A possible new magnetic transition above 77 °K in the ϵ-phase of the Fe–Nb (30 at% Nb) alloy has been found. In FeTe2 a magnetic transition reported earlier from the susceptibility data is confirmed by these Mossbauer studies. The experimental results are explained in terms of the electronic configuration and the structure of these alloys. Isomere Verschiebung, Quadrupolaufspaltung und magnetische Hyperfeinaufspaltung von Eisen wurden in α-Fe–Be-: FeBe5; α-Fe–Nb-, ϵ-Fe–Nb-, α-Fe–Ru-, γ-Fe–Ru-, FeTe2-, α-Fe–Ir- und γ-Fe–Ir-Legierungen mit dem Mosbauereffekt gemessen. Einige dieser Untersuchungen wurden als Funktion der Temperatur im Bereich von 60 bis 300 °K durchgefuhrt. Alle Systeme bis auf FeBe5 und γ-Fe–Ir wurden zum ersten Male untersucht. Ein moglicher neuer magnetischer Ubergang oberhalb 77 °K in der ϵ-Phase der Fe–Nb (30 At% Nb)-Legierung wurde gefunden. In FeTe2 wird ein fruher aus Suszeptibilitatsdaten gefundener magnetischer Ubergang durch diese Mosbaueruntersuchungen bestatigt. Die experimentellen Ergebnisse werden mit der elektronischen Konfiguration und der Struktur dieser Legierungen erklart.