Pt Nanoparticles Embedded in Colloidal Crystal Template Derived 3D Ordered Macroporous Ce0.6Zr0.3Y0.1O2: Highly Efficient Catalysts for Methane Combustion

Three-dimensionally ordered macro/mesoporous Ce0.6Zr0.3Y0.1O2 (3DOM CZY) supported high-dispersion Pt nanoparticles (x wt % Pt/3DOM CZY, x = 0.6, 1.1, and 1.7) were successfully synthesized via the cetyltrimethylammonium bromide/triblock copolymer P123 assisted gas bubbling reduction route. The 3DOM CZY and x wt % Pt/3DOM CZY samples exhibited a high surface area of 84–94 m2/g. Pt nanoparticles (NPs) with a size of 2.6–4.2 nm were uniformly dispersed on the surface of 3DOM CZY. The 1.1 wt % Pt/3DOM CZY sample showed excellent catalytic performance, giving a T90% value at 598 °C at gas hourly space velocity (GHSV) of 30000 mL/(g h) and the highest turnover frequency (TOFPt) of 6.98 × 10–3 mol/(molPt s) at 400 °C for methane combustion. The apparent activation energy (64 kJ/mol) over 1.1 wt % Pt/3DOM CZY was much lower than that (95 kJ/mol) over Bulk CZY. The effects of water vapor and SO2 on the catalytic activity of 1.1 wt % Pt/3DOM CZY were also examined. It is concluded that the excellent catalytic acti...