Short-time hydrothermal synthesis and delamination of ion exchangeable Mg/Ga layered double hydroxides

The hydrothermal synthesis of magnesium–gallium layered double hydroxides (Mg/Ga LDHs) was studied under static and agitated conditions. Not only well-crystallized and large-sized Mg/Ga LDHs having hexagonal morphology were obtained but also the reaction time was comparatively decreased from 24 to 2 h by means of agitation during hydrothermal synthesis. In static conditions, mainly GaOOH and magnesite phases were formed. The elemental analysis results show that the final Mg/Ga ratio is significantly different from the initial ratio. The reason was attributed to the difference in the hydrolytic behavior of Mg2+ and Ga3+. Furthermore, the anion exchange studies with glycine, dodecyl sulfate, ferrocyanide and ferricyanide were performed to investigate the intercalation behavior of the anions into Mg/Ga LDHs. In addition, delamination of Mg/Ga LDHs was performed in formamide for the glycine exchanged forms. Large size of nanosheets thus obtained can be utilized in the fabrication of functional thin films.