First-principles FP-LAPW calculations and X-ray spectroscopy studies of the electronic structure of Zr3V3O and Zr3V3O0.6 oxides

Electronic properties of Zr 3 V 3 O oxide, a very promising hydrogen-storage material, were studied both from theoretical and experimental points of view employing the full potential linearized augmented plane wave (FP-LAPW) method as well as X-ray photoelectron spectroscopy (XPS) and X-ray emission spectroscopy (XES). Total and partial densities of states of the constituting atoms of Zr 3 V 3 O have been derived from the FP-LAPW calculations. These data indicate that, the O 2p-like states are the dominant contributors in the bottom of the valence band, whilst the top of the valence band and the bottom of the conduction band of Zr 3 V 3 O are dominated by contributions of the V2 3d-like states, with slightly smaller contributions of the V1 3d-like states as well. Significant contributions of the Zr 4d-like states throughout the whole valence-band region and near the bottom of the conduction band are also characteristic of the electronic structure of Zr 3 V 3 O. The XPS valence-band spectra and the XES Zr Lβ 2,15 , V L α and O K α bands have been derived and compared on a common energy scale for Zr 3 V 3 O and Zr 3 V 3 O 0.6 oxides. This comparison of the experimental spectra was found to be in excellent agreement with the results of the FP-LAPW calculations. In addition, the XPS Zr 3d, V 2p and O 1s core-level binding energies have been measured for Zr 3 V 3 O and Zr 3 V 3 O 0.6 oxides.