Hydro deformation in ceramic tiles at the pre-firing stage

The production of ceramic tiles with larger sizes and reduced thickness has increased the challenge of producing high-quality ceramic tiles in short single-firing cycles. For porcelain tiles, the pressing step is of upmost importance for the microstructure of the green bodies. The particle size distribution, mineral composition of the pastes and porosity before firing define the water flow during the decoration process. Hydro deformation is the curvature of unfired ceramic tiles caused by water absorption during the decoration step before firing. In this work, the hydro deformation is studied in function of tile thickness, compaction, and clay composition according to a 2K factorial design. Two compositions of porcelain tiles (glazed and polished) were pressed at two thicknesses (3–6 mm) and pressing pressures (35.5–49.8 MPa) forming ceramic tiles with 55 × 110 mm² of surface area. Chemical (XRF), mineralogical (XRD), thermogravimetric (TG), specific surface area (BET), granulometric, bulk density, and porosity analyses were performed for the green tiles of both compositions. To simulate the hydro deformation during the decoration step, the curvature (mm) of the tiles was studied within a 0–180 min interval. The water absorption rate through the surface (g.m−2·s−1) of the tiles in an interval of 0–180 s was studied as a function of thickness, pressure and porcelain tile composition. As a result, the thickness of the tiles can change the curvatures from concave to convex. Pressing conditions and composition of the tiles can change the water absorption rates. Porcelain tiles with higher content of clay minerals develop convex curvatures. For tiles with lower content of clay minerals, concave curvatures were developed.