Influence of Pr-Al-Co alloy diffusion source on magnetic properties and microstructure of sintered Nd-Fe-B magnets processed by grain boundary diffusion

In this study, the influence of the content of Al and Co in the diffusion source on the magnetic performance and microstructure of the diffused magnet was discussed by grain boundary diffusion treatment with Pr70Al30–xCox (x=0 at%, 10 at%, 15 at%, 20 at%, 30 at%) alloys. When the Co content in the diffusion source increases from 0 at% to 10 at%, the coercivity enhancement in the Pr70Al20Co10 diffused magnet is the highest, increased from 1.62 to 2.24 T, higher than 2.01 T of the Pr70Al30 diffused magnet. With the further increase of Co content in the diffused source, the coercivity of the diffused magnet decreases gradually, the coercivity of Pr70Al15Co15, Pr70Al20Co10 and Pr70Co30 diffused magnet is 2.15, 1.99 and 1.81 T, respectively. Microstructural analysis shows that plenty of continuous grain boundary phases (CGBPs) can be formed in the Pr70Al20Co10 diffused magnet under the synergistic effect of Al and Co, which leads to the enhancement of magnetic isolation between more adjacent grains. However, the amount of CGBP in the diffused magnets gradually decreases with the further increase of Co content in the diffusion source.